TAMCRETE® ERM 75
TAMCRETE® ERM75 is a two-component, solvent-free, moisture-tolerant, thixotropic, high-strength epoxy adhesive, anchoring and structural repair mortar containing epoxy resin and special fillers.
Complies with EN 1504-3 and EN 1504-6 standards.
EN 1504-6: Product for anchoring of reinforcing steel bar
Areas of Application
● Anchoring and installation applications on concrete and stone surfaces
● Reinforcement anchoring and fixing
● Filling and injection of wide cracks
● Structural concrete repairs
● Steel-to-concrete connection details
● Bonding expansion joint tapes
Advantages
● Easy to prepare and apply
● Provides high mechanical strength
● Exhibits excellent adhesion to various substrates
● Thixotropic consistency, does not sag
● Cures without shrinkage
● Provides high early and ultimate strength
● High abrasion resistance
● Impermeable to water and water vapor
● Resistant to chemicals
● Moisture tolerant
● Excellent adhesion to concrete and metal
● Solvent-free
|
General Information |
|
|
Material composition |
Epoxy resin and special fillers |
|
Appearance |
Grey-colored, paste consistency |
|
Density (mixed) |
~1.77 kg/lt |
|
Performance Data (EN 1504-3 / EN 1504-6) |
|
|
Compressive strength (EN 12190) |
≥ 30 N/mm² (1 day), ≥ 75 N/mm² (7 days) |
|
Flexural strength (EN 196-1) |
≥ 17 N/mm² (1 day), ≥ 25 N/mm² (7 days) |
|
Bond strength (EN 1542) |
To concrete ≥ 3.0 N/mm², to metal ≥ 3.5 N/mm² |
|
Pull-out resistance (EN 1881) |
≤ 0.6 mm displacement (under 75 kN load) |
|
Application Data |
|
|
Application temperature |
+10°C / +30°C |
|
Service temperature |
−15°C / +90°C |
|
Mixing ratio |
A: 3.75 kg / B: 1.25 kg |
|
Pot life |
~40 min |
|
Application thickness |
2–30 mm (single layer) |
|
Initial hardening |
~12 hours |
|
Full cure |
7 days |
|
Consumption |
~1.7 kg/m² (1 mm thickness) |
|
Safety Information |
|
|
Hazardous substances |
Refer to SDS |
The stated technical values are obtained at +23°C ambient temperature and 50% relative humidity conditions. High temperatures shorten the time, low temperatures extend it.